ASTM B505 C93900 / C939 / CDA939
Chemical composition
| % min | % máx | |
|---|---|---|
| Cu | 76.5 | 79.5 |
| Sn | 5.0 | 7.0 |
| Pb | 14.0 | 18.0 |
| Zn | 1.5 | |
| Fe | 0.40 | |
| Ni | 0.80 | |
| Al | 0.005 | |
| Sb | 0.5 | |
| S | 0.08 | |
| P | 1.5 | |
| Si | 0.005 |
Sum of Named Elements 98.9% min.
Mechanical properties (Minimum values)
| Tensile Strength, Min | Ksi | 25 |
|---|---|---|
| Mpa | 172 | |
| Yield Strength, at 0,5 % Extension Under Load Min | Ksi | 16 |
| Mpa | 110 | |
| Elongation in 2 in. Or 50mm, min % | 5 | |
Applications
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| IndustrialBearings | Corrosion Resistance | Corrosion Resistance | |
| Bearings | Corrosion Resistance | Corrosion Resistance to Brackish Water | |
| Bearings | Corrosion Resistance | Corrosion Resistance to Many Industrial Chemicals | |
| Bearings | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
| Bearings | Machining Properties | Machinability, Good | |
| Bearings | Mechanical Properties | Relatively Low Strength | |
| Pump Bodies | Corrosion Resistance | Corrosion Resistance | |
| Pump Bodies | Corrosion Resistance | Corrosion Resistance to Brackish Water | |
| Pump Bodies | Corrosion Resistance | Corrosion Resistance to Many Industrial Chemicals | |
| Pump Bodies | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
| Pump Bodies | Machining Properties | Machinability, Good | |
| Pump Bodies | Mechanical Properties | Relatively Low Strength | |
| Pump Impellers for Mine Water | Corrosion Resistance | Corrosion Resistance | |
| Pump Impellers for Mine Water | Corrosion Resistance | Corrosion Resistance to Brackish Water | |
| Pump Impellers for Mine Water | Corrosion Resistance | Corrosion Resistance to Many Industrial Chemicals | |
| Pump Impellers for Mine Water | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
| Pump Impellers for Mine Water | Machining Properties | Machinability, Good | |
| Pump Impellers for Mine Water | Mechanical Properties | Relatively Low Strength |