Project Description
W-AlFe
EN 1982 CC331GCuAl10Fe2-C
- Copper based alloy with aluminium and iron as principal elements.
- Extremely hard and tough material with high static and dynamic resistance, sea water, corrosion and erosion resistance. Good performance at high temperature.
- Bronze alloy for mechanical components subjected to forces between -200 a +200ºC The closest international standard is the ASTM B505 C95200
- Wisco has a large stock of rectangular bars and round solid and hollow bars with immediate availability.
Chemical composition
% min. | % máx | |
---|---|---|
Al | 8,5 | 10,5 |
Cu | 83,0 | 89,5 |
Fe | 1,5 | 3,5 |
Mn | 1,0 | |
Ni | 1,5 | |
Mg | 0,05 | |
Pb | 0,10a | |
Si | 0,2 | |
Sn | 0,20 | |
Zn | 0,50 |
a For castings intended to be welded, the maximum lead content shall be 0,03 %.
Mechanical properties (Minimum values)
Moulding process and nomination | Continuous (GC)1 | Centrifugal (GZ) |
---|---|---|
Tensile Strength Rm (MPa) |
550 | 550 |
Yield Point 0,2% Rp0,2 (MPa) |
200 | 200 |
Elongation 5D A (%) |
15 | 18 |
HBW (10-1000) | 130 | 130 |
1For pieces with an exterior diameter of ≤ 300 mm. For larger sizes values to be agreed with the order.
Physical properties
Density kg/dm3 |
7,5 |
---|---|
Specific Heat J/(g*K) |
0,420 |
Thermal Expansion 10-6 K |
16 – 17 |
Thermal Conductivity W/(m*K) |
55 |
Electrical Conductivity MS/m |
5 a 8 |
Applications
Categoría | Producto | Categoría Razón | Razón |
---|---|---|---|
Electrical | Electrical Hardware | Conductivity (Thermal) | Thermal Conductivity |
Electrical Hardware | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Electrical Hardware | Mechanical Properties | High Strength | |
Fasteners | Nuts | Corrosion Resistance | Corrosion Resistance (Excellent) |
Nuts | Machining Properties | Machinability, Good | |
Nuts | Mechanical Properties | High Strength | |
Industrial | Acid Resistant Pumps | Corrosion Resistance | Corrosion Resistance (Excellent) |
Acid Resistant Pumps | Corrosion Resistance | Corrosion Resistance to Acidss | |
Acid Resistant Pumps | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
Acid Resistant Pumps | Corrosion Resistance | Corrosion Resistance to Saline Solutions | |
Acid Resistant Pumps | Friction & Wear Properties | Wear Resistance | |
Acid Resistant Pumps | Machining Properties | Machinability, Good | |
Acid Resistant Pumps | Mechanical Properties | High Strength | |
Bearing Liners | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Bearing Liners | Friction & Wear Properties | Wear Resistance | |
Bearing Liners | Mechanical Properties | High Strength | |
Bearings | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Bearings | Friction & Wear Properties | Wear Resistance | |
Bearings | Machining Properties | Machinability, Good | |
Bearings | Mechanical Properties | High Strength | |
Bushings | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Bushings | Friction & Wear Properties | Wear Resistance | |
Bushings | Machining Properties | Machinability, Good | |
Bushings | Mechanical Properties | High Strength | |
Gears | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Gears | Friction & Wear Properties | Wear Resistance | |
Gears | Machining Properties | Machinability, Good | |
Gears | Mechanical Properties | High Strength | |
High Strength Clamps | Corrosion Resistance | Corrosion Resistance | |
High Strength Clamps | Mechanical Properties | High Strength | |
Hot Mill Guides | Conductivity (Thermal) | Thermal Conductivity | |
Hot Mill Guides | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Hot Mill Guides | Friction & Wear Properties | Wear Resistance | |
Hot Mill Guides | Mechanical Properties | High Strength | |
Hot Mill Guides | Mechanical Properties | Retains Strength at Elevated Temperatures | |
Hydrant Parts | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Hydrant Parts | Corrosion Resistance | Corrosion Resistance to Brackish Water | |
Hydrant Parts | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
Hydrant Parts | Friction & Wear Properties | Wear Resistance | |
Hydrant Parts | Machining Properties | Machinability, Good | |
Hydrant Parts | Mechanical Properties | High Strength | |
Large Gear Parts | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Large Gear Parts | Friction & Wear Properties | Wear Resistance | |
Large Gear Parts | Mechanical Properties | High Strength | |
Mild Alkali Applications | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Mild Alkali Applications | Corrosion Resistance | Corrosion Resistance to Acids | |
Mild Alkali Applications | Friction & Wear Properties | Wear Resistance | |
Mild Alkali Applications | Mechanical Properties | High Strength | |
Pickling Equipment | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Pickling Equipment | Corrosion Resistance | Corrosion Resistance to Acids | |
Pickling Equipment | Machining Properties | Machinability, Good | |
Pickling Equipment | Mechanical Properties | High Strength | |
Pickling Tanks | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Pickling Tanks | Corrosion Resistance | Corrosion Resistance to Acids | |
Pickling Tanks | Friction & Wear Properties | Wear Resistance | |
Pickling Tanks | Mechanical Properties | High Strength | |
Plungers | Corrosion Resistance | Wear Resistance | |
Plungers | Friction & Wear Properties | Wear Resistance | |
Plungers | Machining Properties | Machinability, Good | |
Plungers | Mechanical Properties | High Strength | |
Pump Parts | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Pump Parts | Corrosion Resistance | Corrosion Resistance to Acids | |
Pump Parts | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
Pump Parts | Corrosion Resistance | Corrosion Resistance to Saline Solutions | |
Pump Parts | Friction & Wear Properties | Wear Resistance | |
Pump Parts | Machining Properties | Machinability, Good | |
Pump Parts | Mechanical Properties | High Strength | |
Pump Rods | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Pump Rods | Friction & Wear Properties | Wear Resistance | |
Pump Rods | Machining Properties | Machinability, Good | |
Pump Rods | Mechanical Properties | High Strength | |
Thrust Pads | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Thrust Pads | Friction & Wear Properties | Wear Resistance | |
Thrust Pads | Mechanical Properties | High Strength | |
Valve Bodies | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Valve Bodies | Friction & Wear Properties | Wear Resistance | |
Valve Bodies | Machining Properties | Machinability, Good | |
Valve Bodies | Mechanical Properties | High Strength | |
Valve Seats | Corrosion Resistance | Corrosion Resistance | |
Valve Seats | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Valve Seats | Friction & Wear Properties | Wear Resistance | |
Valve Seats | Machining Properties | Machinability, Good | |
Valve Seats | Mechanical Properties | High Strength | |
Valves | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Valves | Friction & Wear Properties | Wear Resistance | |
Valves | Machining Properties | Machinability, Good | |
Valves | Mechanical Properties | High Strength | |
Wear Plates | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Wear Plates | Friction & Wear Properties | Wear Resistance | |
Wear Plates | Mechanical Properties | High Strength | |
Welding Jaws | Conductivity (Thermal) | Thermal Conductivity | |
Welding Jaws | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Welding Jaws | Mechanical Properties | High Strength | |
Welding Jaws | Mechanical Properties | Retains Strength at Elevated Temperatures | |
Worm Wheels | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Worm Wheels | Friction & Wear Properties | Wear Resistance | |
Worm Wheels | Machining Properties | Machinability, Good | |
Worm Wheels | Mechanical Properties | High Strength | |
Worms | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Worms | Friction & Wear Properties | Wear Resistance | |
Worms | Machining Properties | Machinability, Good | |
Worms | Mechanical Properties | High Strength | |
Marino | Covers for Marine Hardware | Appearance | Appearance |
Covers for Marine Hardware | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Covers for Marine Hardware | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
Covers for Marine Hardware | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Covers for Marine Hardware | Mechanical Properties | High Strength | |
Marine Engines | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Marine Engines | Corrosion Resistance | Corrosion Resistance to Brackish Water | |
Marine Engines | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
Marine Engines | Friction & Wear Properties | Wear Resistance | |
Marine Engines | Mechanical Properties | Fatigue Properties | |
Marine Engines | Mechanical Properties | High Strength | |
Marine Hardware | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Marine Hardware | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
Marine Hardware | Corrosion Resistance | Corrosion Resistance to Saline Solutions | |
Marine Hardware | Mechanical Properties | High Strength | |
Propellers | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Propellers | Corrosion Resistance | Corrosion Resistance to Brackish Water | |
Propellers | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
Propellers | Friction & Wear Properties | Wear Resistance | |
Propellers | Mechanical Properties | High Strength | |
Propellers | Mechanical Properties | Retains Strength at Elevated Temperatures | |
Ordnance | Gun Mountings | Corrosion Resistance | Corrosion Resistance (Excellent) |
Gun Mountings | Friction & Wear Properties | Wear Resistance | |
Gun Mountings | Mechanical Properties | High Strength | |
Gun Slides | Corrosion Resistance | Corrosion Resistance (Excellent) | |
Gun Slides | Friction & Wear Properties | Wear Resistance | |
Gun Slides | Mechanical Properties | High Strength |
Closest international standards
Area | Standards | Alloy | Code | Former denomination | Status |
---|---|---|---|---|---|
Europe | BS 1400 | AB1 | Annulled | ||
DIN 1714 | CuAl10Fe | Annulled | |||
NFA-53709 | CuAl10Fe3 | Annulled | |||
USA | ASTM B505 | C95200 | In force | ||
ASTM B271 | C95200 | In force | |||
Australia | AS 1565 | C95210 | In force | ||
Japan | JIS H5121 | CAC701C | In force | ||
JIS H5120 | CAC701C | In force | |||
ISO | 1338 | CuAl10Fe3 | Annulled | ||
Germany | DIN 1705 : 1981 | CuSn7ZnPb | 2.1090 | Rg 7, GC-Rg 7, GZ- Rg 7 | |
Australia | AS 1565 : 1996, AS 2738-3 : 1984-00 | C92410A | C92410A | 87/ 7/ 3/ 3 Leaded gunmetal | |
Australia | AS 1565 : 1996 | C93200 | C93200 | Leaded gunmetal SAE 660 | |
Denmark | DS 3001 : 1978 | Rodgods 5426 | 5426 | Rodgods 5426 [ Rg 7 ] | |
Spain | UNE 37-103-2 : 1981 | CuSn7Zn4Pb6 | C-3530 | ||
Europe | EN 1982 : 1998 | CuSn7Zn2Pb3-C | CC492K | ||
Europe | EN 1982 : 1998 | CuSn7Zn4Pb7-C | CC493K | ||
Finland | SFS 2207 : 1977 | CuSn7Pb6Zn3 | |||
France | NF A 53-707 : 1987 | CuSn7Pb6Zn4 | |||
ISO | ISO 1338 : 1977 | CuSn7Zn3Pb7 | BS ZN 4 // Bronzo allo zinco | ||
Italy | UNI 7013-7 : 1972 | ||||
Portugal | NS 16525 : 1977 | CuSn7Pb6Zn3 | Rodmetall Stopelegering | ||
Portugal | NP 1585 : 1978 | CuSn7Pb6Zn4 | |||
UK | BS 1400 : 1985 | CuSn7Pb3Zn3 | LG4 | 87/7/3/3 Leaded gunmetal CuSn7 | |
Switzerland | VSM 10810-1 : 1973 | CuSn7Pb6Zn4 | Rg 7 | ||
USA | ASTM B 584 : 1999 | C93200 | C93200 | High-lead tin bronze SAE 660 | |
Germany | DIN 1714 : 1981 | CuAl10Fe | 2.0940 | G-FeAlBz F50 | |
Australia | AS 1565 : 1996 | C95210 | C95210 | Aluminium bronze [ 952C ] | |
China | GOST 493 : 1979 / 85 | BrA9Z3L | |||
China | GB 1176 : 1987 | CuAl10Fe3 | 10 – 3 Alu Bronze | ||
Spain | UNE 37-103-2 : 1981 | C-4210 | CuAl10Fe3 | ||
Finland | SFS 2211 : 1977 | CuAl10Fe3 | |||
France | NF A 53-707 : 1987 | CuAl10Fe3 | |||
Hungary | MSZ 8579 : 1984 | CuAl9Fe3 | Albzö 9-3 | ||
ISO | ISO 1338 : 1977 | CuAl10Fe3 | |||
Japan | JIS H 5114 : 1988 | Class 1 | Al BC 1 | ||
Norway | NS 16575 : 1977 | CuAl10Fe3 | Aluminiumbronse Stopelegering | ||
Portugal | NP 1213 : 1976 | CuAl10Fe3 | Bronze de aluminio para fundic | ||
UK | BS 1400 : 1985 | AB1 | CuAl10Fe3 | Aluminium bronze CuAl10Fe3 | |
Sweden | SIS 145710 : 1977 | CuAl10Fe3 | 5710 | Aluminiumbrons 5710 | |
Switzerland | VSM 10810-3 : 1973 | CuAl10Fe3 | |||
USA | ASTM B 148 : 1997 | C95200 | C95200 | Aluminium bronze SAE 68A |
Optional thermal treatments available on clients’ request
- Stabilised.