Project Description
ASTM B271 C86200
Closest alloysEN 1982 CC764S
CuZn34Mn3Al2Fe1-C
Chemical composition
% min | % máx | |
---|---|---|
Cu | 60.0 | 66.0 |
Sn | 0.2 | |
Pb | 0.2 | |
Zn | 22.0 | 28.0 |
Fe | 2.0 | 4.0 |
Ni | 1.0 | |
Al | 3.0 | 4.9 |
Mn | 2.5 | 5.0 |
Sum of Named Elements 99.0% min.
Mechanical properties (Minimum values)
Tensile Strength, Min | Ksi | 90 |
---|---|---|
Mpa | 621 | |
Yield Strength, at 0,5 % Extension Under Load Min | Ksi | 45 |
Mpa | 310 | |
Elongation in 2 in. Or 50mm, min % | 18 |
Applications
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Builders Hardware | Brackets | Corrosion Resistance | Corrosion Resistance |
Brackets | Mechanical Properties | Moderate Strength | |
Structural Parts | Corrosion Resistance | Corrosion Resistance | |
Structural Parts | Mechanical Properties | Moderate Strength | |
Fasteners | Screw Down Nuts | Corrosion Resistance | Corrosion Resistance |
Screw Down Nuts | Friction & Wear Properties | Wear Resistance | |
Screw Down Nuts | Mechanical Properties | Moderate Strength | |
Industrial | Bushings | Corrosion Resistance | Corrosion Resistance |
Bushings | Friction & Wear Properties | Wear Resistance | |
Bushings | Mechanical Properties | Moderate Strength | |
Cams | Corrosion Resistance | Corrosion Resistance | |
Cams | Friction & Wear Properties | Wear Resistance | |
Cams | Mechanical Properties | Moderate Strength | |
Frames | Corrosion Resistance | Corrosion Resistance | |
Frames | Friction & Wear Properties | Wear Resistance | |
Frames | Mechanical Properties | Moderate Strength | |
Gears | Corrosion Resistance | Corrosion Resistance | |
Gears | Friction & Wear Properties | Wear Resistance | |
Gears | Mechanical Properties | Moderate Strength | |
High Strength Machine Parts | Conductivity (Thermal) | Thermal Conductivity | |
High Strength Machine Parts | Corrosion Resistance | Corrosion Resistance | |
High Strength Machine Parts | Corrosion Resistance | Corrosion Resistance to the Atmosphere | |
High Strength Machine Parts | Friction & Wear Properties | Wear Resistance | |
High Strength Machine Parts | Mechanical Properties | Moderate Strength | |
Hooks | Corrosion Resistance | Corrosion Resistance | |
Hooks | Mechanical Properties | Moderate Strength | |
Marine Racing Propellers | Corrosion Resistance | Corrosion Resistance | |
Marine Racing Propellers | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Marine Racing Propellers | Corrosion Resistance | Corrosion Resistance to the Atmosphere | |
Marine Racing Propellers | Friction & Wear Properties | Wear Resistance | |
Marine Racing Propellers | Mechanical Properties | Moderate Strength | |
Pressing Dies for Wood Pulp | Corrosion Resistance | Corrosion Resistance | |
Pressing Dies for Wood Pulp | Friction & Wear Properties | Wear Resistance | |
Pressing Dies for Wood Pulp | Mechanical Properties | Moderate Strength | |
Shafts | Corrosion Resistance | Corrosion Resistance | |
Shafts | Friction & Wear Properties | Wear Resistance | |
Shafts | Mechanical Properties | Moderate Strength | |
Struts | Corrosion Resistance | Corrosion Resistance | |
Struts | Corrosion Resistance | Corrosion Resistance to the Atmosphere | |
Struts | Friction & Wear Properties | Wear Resistance | |
Struts | Mechanical Properties | Moderate Strength | |
Valve Stems | Corrosion Resistance | Corrosion Resistance | |
Valve Stems | Friction & Wear Properties | Wear Resistance | |
Valve Stems | Mechanical Properties | Moderate Strength | |
Wear Rings for Pressing Dies for Wood Pulp Industry | Corrosion Resistance | Corrosion Resistance | |
Wear Rings for Pressing Dies for Wood Pulp Industry | Friction & Wear Properties | Wear Resistance | |
Wear Rings for Pressing Dies for Wood Pulp Industry | Mechanical Properties | Moderate Strength | |
Worm Gears | Corrosion Resistance | Corrosion Resistance | |
Worm Gears | Friction & Wear Properties | Wear Resistance | |
Worm Gears | Mechanical Properties | Moderate Strength | |
Marine | Boat Parts | Corrosion Resistance | Corrosion Resistance |
Boat Parts | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Boat Parts | Corrosion Resistance | Corrosion Resistance to the Atmosphere | |
Boat Parts | Friction & Wear Properties | Wear Resistance | |
Boat Parts | Mechanical Properties | Moderate Strength | |
Clamps | Corrosion Resistance | Corrosion Resistance | |
Clamps | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Clamps | Mechanical Properties | Moderate Strength | |
Marine Castings | Corrosion Resistance | Corrosion Resistance | |
Marine Castings | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Marine Castings | Corrosion Resistance | Corrosion Resistance to the Atmosphere | |
Marine Castings | Friction & Wear Properties | Wear Resistance | |
Marine Castings | Mechanical Properties | Moderate Strength | |
Rudders | Corrosion Resistance | Corrosion Resistance | |
Rudders | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Rudders | Corrosion Resistance | Corrosion Resistance to the Atmosphere | |
Rudders | Friction & Wear Properties | Wear Resistance | |
Rudders | Mechanical Properties | Moderate Strength | |
Ordnance | Gun Mounts | Appearance | Appearance |
Gun Mounts | Corrosion Resistance | Corrosion Resistance | |
Gun Mounts | Friction & Wear Properties | Wear Resistance | |
Gun Mounts | Mechanical Properties | Moderate Strength |