CC334G
CuAl11FeNi6-CAluminium Copper Alloy
Chemical composition
| % min. | % máx | |
|---|---|---|
| Ala | 10,0 | 12,0 |
| Cua | 72,0 | 82,5 |
| Fea | 4,0 | 7,0 |
| Mn | 2,5 | |
| Ni | 4,0 | 7,5 |
| Mg | 0,05 | |
| Pb | 0,05 | |
| Si | 0,1 | |
| Sn | 0,02 | |
| Zn | 0,50 |
a For permanent mould castings, the minimum iron content of ingots and castings shall be 3,0 % and the minimum
aluminium content shall be 9,0 %. In this case, the maximum copper content shall be 84,5 %.
Mechanical properties (Minimum values)
| Casting method and alloy description | Continuous (GC) | Centrifugal (GZ) |
|---|---|---|
| Tensile Strength, Min A (MPa) | 750 | |
| Yield Strength 0,2% Rp0,2 (MPa) |
380 | |
| Elongation A (%) |
5 | |
| Brinell Hardness HBW (10-1000) | 185 |